Structural, electrical and optical properties of Al–Sn codoped ZnO transparent conducting layer deposited by spray pyrolysis technique
Résumé
Low cost Al-Sn codoped ZnO (ATZO) Transparent Conductive Oxide films were deposited by spray pyrolysis on glass substrate. The influence of Al-Sn codoping on the structural, optical and electrical properties of ZnO thin films was studied by comparing the same properties obtained in undoped ZnO, Al doped ZnO (AZO) and Sn doped ZnO (TZO) thin films. The so-obtained films crystallized in hexagonal wurtzite structure. The morphology and structural defects have been investigated by both High resolution Field Effect Scanning Electron Microscopy (FE-SEM) and Raman spectroscopy at 532 nm excitation source. In the visible region, the undoped and doped films show an average transmittance of the order of 85%, while for ATZO thin film, it is of the order of 72%, which points out a degradation of the optical properties due to the co-doping. The optical band gap of ATZO thin film achieves 3.31eV and this shift, compared to the referred samples is attributed to the Burstein–Moss (BM) and band gap narrowing (BGN) opposite effects which is due to the increase of the carrier concentration in degenerate semiconductors. Within all the samples, the ATZO thin film exhibits the lowest electrical resistivity of 4.56 × 10−3 Ωcm with a Hall mobility equal to 2.13 cm2 V−1s−1, and the highest carrier concentration of 6.41 × 1020 cm−3. The performance of ATZO transparent conductive oxide film are determined by its figure of merit (φTC), found equal to 1.69 10−4 Ω−1, which is a suitable value for potentially high-performance solar cell applications.