Apatitic calcium phosphates: Synthesis, characterization and reactivity in the removal of lead(II) from aqueous solution

Doan Pham Minh (1) , Haroun Sebei (1) , Ange Nzihou (1) , Patrick Sharrock (1)

1 RAPSODEE - Centre de recherche d'Albi en génie des procédés des solides divisés, de l'énergie et de l'environnement

The synthesis of calcium hydroxyapatite (Ca-HA, chemical formula Ca-10(PO4)(6)(OH)(2)) from calcium carbonate and orthophosphoric acid was investigated under atmospheric conditions to determine their suitability as economical starting materials. The order in which reactants were added influenced only the particle size distribution of the solid products. Calcium carbonate particles were rapidly dissolved in acid medium of orthophosphoric acid. The divalent calcium formed was then precipitated with orthophosphate species to form small primary calcium phosphate particles (<1 mu m) which partially agglomerated into larger particles with a particle size of up to 300 um. The dissolution of calcium carbonate was not complete, even after a long reaction time of 72 h and large particles with core-shell structures were formed from residual calcium carbonate particles (core) and calcium phosphate based compounds (shell). Using different characterization techniques, the principal intermediates of the reaction could be identified including mono-calciumphosphate monohydrate (MCPM. Ca(H2PO4)(2)center dot H2O), dicalcium phosphate dihydrate (DCPD, CaHPO4 center dot 2H(2)O), dicalcium phosphate anhydrous (DCPAs) and octacalcium bis(hydrogenphosphate) tetrakis(phosphate) pentahydrate (OCP, Ca-8(HPO4)(2)(PO4)(4)center dot 5H(2)O). Their evolution during the synthesis was followed. The final products obtained after 72 h of synthesis contained a mixture of Ca-HA, OCP, B-type calcium carbonate-apatite (CAP, Ca-10(PO4)(6)CO3) with low crystallinity and some small amounts of intermediates. The removal of Pb2+ ions, used as a model pollutant, was performed with the calcium phosphate sorbents in powder form or in suspension form. The highest sorption capacity was found at 625 mg g(-1) for the sorbent in suspension form which resulted from the addition of calcium carbonate powder to the solution of orthophosphoric acid. From the identification of the composition of the sorbents, the reaction pathway for the removal of lead(II) is proposed. (C) 2012 Elsevier B.V. All rights reserved.

Mots clés: Mechanism; Calcium hydroxyapatite; Characterization; One-step synthesis; Kinetic sorption

Domaines: Sciences de l'ingénieur [physics]

Doan Pham Minh, Haroun Sebei, Ange Nzihou, Patrick Sharrock. Apatitic calcium phosphates: Synthesis, characterization and reactivity in the removal of lead(II) from aqueous solution. Chemical Engineering Journal, 2012, 198, p. 180-190. ⟨10.1016/j.cej.2012.05.083⟩. ⟨hal-01632405⟩