Origin of epoxies embrittlement during oxidative ageing

Résumé

Thermal oxidation of three epoxy resins prepared from flexible or rigid prepolymers and hardeners was studied by monitoring epoxy mechanical and physical changes. The physical changes were followed by mass measurements, glass transition temperature using DSC and sub-glass β transition using DMA. It was put in evidence that embrittlement is not directly associated to Tg or mass loss changes since epoxy network based on isophorone diamine (IPDA) hardeners were shown to undergo mainly a chain scission at the beginning of exposure process whereas epoxy network based on trioxatridecane diamine (TTDA) hardeners exhibits a crosslinking process with a significant mass loss. The only common feature for both epoxy systems to understand embrittlement is the drop of amplitude of β transition with oxidation.
Fichier principal
Vignette du fichier
PIMM - PT - ERNAULT - 2017.pdf (1.25 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01593556 , version 1 (26-09-2017)

Identifiants

Citer

Esteve Ernault, Emmanuel Richaud, Bruno Fayolle. Origin of epoxies embrittlement during oxidative ageing. Polymer Testing, 2017, 63, pp.448-454. ⟨10.1016/j.polymertesting.2017.09.004⟩. ⟨hal-01593556⟩
65 Consultations
276 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More