Large electrocaloric strength and broad electrocaloric temperature span in lead-free Ba 0.85 Ca 0.15 Ti 1Àx Hf x O 3 ceramics

Résumé

The electrocaloric (EC) effect of Ba 0.85 Ca 0.15 Ti 1Àx Hf x O 3 (abbreviated as: BCTH x) ceramics has been systematically investigated using an indirect method. Our results indicate that the BCTH 0.06 ceramic exhibits a sharp ferroelectric–paraelectric phase transition, around which a large EC value of 1.03 K is obtained under the electric field of 35 kV cm À1 , associated with a relatively broad electrocaloric temperature span. The giant EC strength of the BCTH 0.06 ceramic is 0.29–0.31 K mm kV À1 under an external electric field of 9 to 35 kV cm À1 , which is larger than most previous values. The temperature of the EC peak shifts to higher temperature as the electric field increases, which implies that electric field may be another powerful tool to obtain a large EC value and modulate the EC peak. The ceramics with higher Hf contents display a strong diffusive character. The BCTH 0.15 ceramic shows a relatively small EC strength (0.10–0.13 K mm kV À1) with a broader EC temperature span. The diffusive feature of the BCTH x ceramics with high Hf concentrations broaden the electrocaloric temperature span and meanwhile decrease the EC strength considerably. Our results indicate that compositional modification in BaTiO 3-based ceramics offers a promising route for designing potential dielectric cooling materials with excellent EC properties.
Fichier principal
Vignette du fichier
c6ra27628h.pdf (1.72 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-01486596 , version 1 (24-08-2020)

Licence

Paternité

Identifiants

Citer

Xiangjian Wang, Jiagang Wu, Brahim Dkhil, Chunlin Zhao, Tangyuan Li, et al.. Large electrocaloric strength and broad electrocaloric temperature span in lead-free Ba 0.85 Ca 0.15 Ti 1Àx Hf x O 3 ceramics. RSC Advances, 2017, ⟨10.1039/c6ra27628h⟩. ⟨hal-01486596⟩
197 Consultations
33 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More