Abstract : The characteristic damage mechanisms of a four-layer plain weave glass fiber/epoxy matrix composite are analyzed by means of optical microscope observations on the edge of a rectangular specimen under tensile loading. Digital image correlation is used to determine the size of transverse yarn cracks and yarn-yarn debonding around the crack tips. An algorithm based on Finite Fracture Mechanics is proposed to model crack and debond initiation and propagation in the composite, which takes into account possible couplings between the cracks. The predicted debond and crack densities are in good agreement with the experimental observations.
Type de document :
Article dans une revue
Composites Part A: Applied Science and Manufacturing, Elsevier, 2017, 96, pp.77-88. 〈10.1016/j.compositesa.2017.02.018〉
Liste complète des métadonnées

Littérature citée [45 références]  Voir  Masquer  Télécharger

https://hal.archives-ouvertes.fr/hal-01480982
Contributeur : François Hild <>
Soumis le : jeudi 2 mars 2017 - 09:24:59
Dernière modification le : jeudi 15 novembre 2018 - 08:39:00
Document(s) archivé(s) le : mercredi 31 mai 2017 - 12:59:42

Fichier

COMPA2017-ccsd.pdf
Fichiers produits par l'(les) auteur(s)

Identifiants

Citation

Aurélien Doitrand, Christian Fagiano, François Hild, Vincent Chiaruttini, Anne Mavel, et al.. Mesoscale analysis of damage growth in woven composites. Composites Part A: Applied Science and Manufacturing, Elsevier, 2017, 96, pp.77-88. 〈10.1016/j.compositesa.2017.02.018〉. 〈hal-01480982〉

Partager

Métriques

Consultations de la notice

190

Téléchargements de fichiers

134