Effect of fibers alignment on the failure of composites in compression in the fiber direction

Influence de l'alignement des fibres sur la rupture des composites en compression sens fibre

Gabriel Eyer (1) , Olivier Montagnier (1, 2) , Jean-Paul Charles (1) , Christian Hochard (1) , Frédéric Mazerolle (1)

1 M&S - Matériaux et Structures
2 CReA - Centre de recherche de l'armée de l'air

The influence of misalignment of fibers on compressive strength in fiber direction for unidirectional carbon fiber reinforced epoxy materials is investigated by an experimental approach. In a first time, results obtained previously are presented. Theses results show that transverse damage decreases significantly the compressive strength. In a second time, theses results are applied to the case of samples wherein the fibers are misaligned. In this case, it will be shown that the problem becomes complex because misalignment of fibers and transverse damage are coupled.

L'étude expérimentale proposée analyse l'influence de l'alignement des fibres sur la résistance en compression sens fibre pour des composites unidirectionnels carbone/époxe. Dans un premier temps, des résultats déjà acquis seront pré-sentés. Ces résultats montreront que l'endommagement abaisse significativement la résistance en compression sens fibre. Dans un second temps, ces résultats seront appliqués au cas de la compression avec des éprouvettes présentant un défaut d'alignement. Il sera montré que, dans ce cas, le problème devient complexe puisqu'il couple alignement des fibres et endommagement matriciel. The influence of misalignment of fibers on compressive strength in fiber direction for unidirectional carbon fiber reinforced epoxy materials is investigated by an experimental approach. In a first time, results obtained previously are presented. Theses results show that transverse damage decreases significantly the compressive strength. In a second time, theses results are applied to the case of samples wherein the fibers are misaligned. In this case, it will be shown that the problem becomes complex because misalignment of fibers and transverse damage are coupled.

Domaines: Matériaux; Matériaux et structures en mécanique [physics.class-ph]; Mécanique des solides [physics.class-ph]; Mécanique des structures [physics.class-ph]; Mécanique des matériaux [physics.class-ph]

Gabriel Eyer, Olivier Montagnier, Jean-Paul Charles, Christian Hochard, Frédéric Mazerolle. Influence de l'alignement des fibres sur la rupture des composites en compression sens fibre. Les Journées Nationales des Composites, Jun 2015, Lyon, France. ⟨hal-01308020⟩