Fluidised bed agglomeration of particles with different glass transition temperatures

Résumé

Fluidised bed agglomeration of particles consists in spraying liquid drops (water or binder solution) on the surface of particles, fluidised by hot air, in order to create sticky regions to allow formation of agglomerates when the sticky particles collide. Many parameters influence agglomerate growth, especially those controlling the particle circulation, and the water and temperature conditions within the bed that determine drying and particle stickiness linked to the glass transition of amorphous components and to the viscosity of moist zones at the particle surface. Maltodextrin DE12 and DE21 particles with different glass transition temperature domains were agglomerated in a batch bench scale fluidised bed, under constant mechanical constraints, changing the sprayed water feed rate and the fluidisation air temperature in order to investigate the influence of particle stickiness on agglomerate growth kinetics and mechanism. The two powders showed a different sensitivity to the water and temperature constraints applied. Whilst for maltodextrin DE12, the size and growth rate increased significantly with the sprayed water flow rate, only a small variation was observed for maltodextrin DE21. In both cases, agglomeration occurred in two stages: firstly, the association of initial particles and secondly the agglomeration of intermediate agglomerates into larger and more porous structures. The change from one growth mechanism to the other depended on the conditions, and influenced the size distribution and structure of agglomerates.
Fichier non déposé

Dates et versions

hal-01269158 , version 1 (05-02-2016)

Identifiants

Citer

Carlos Aviles, Elisabeth Dumoulin, Christelle Turchiuli. Fluidised bed agglomeration of particles with different glass transition temperatures. Powder Technology, 2015, 270, pp.445-452. ⟨10.1016/j.powtec.2014.03.026⟩. ⟨hal-01269158⟩
224 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More