Identification of the metallurgical parameters explaining the corrosion susceptibility in a 2050 aluminium alloy

Abstract : The corrosion behaviour of a 2050 aluminium alloy was studied in a NaCl solution. The structure ofprecipitation did not fully explain the susceptibility to intergranular (in the -T34 state) and intragran-ular corrosion for the aged state (the -T8 state). A relationship between the nature of interfaces, thegrains characteristics (size, internal misorientation and orientation according to the plane exposed tothe electrolyte) on one hand and the corrosion susceptibility of the alloy on the other hand was clearlyestablished. Galvanic coupling between grains with different internal misorientations helped to explainthe intergranular corrosion susceptibility of the -T34 state.
Document type :
Journal articles
Complete list of metadata

https://hal.archives-ouvertes.fr/hal-01264384
Contributor : Open Archive Toulouse Archive Ouverte (oatao) <>
Submitted on : Friday, March 4, 2016 - 10:13:42 AM
Last modification on : Friday, January 10, 2020 - 9:08:22 PM
Long-term archiving on: : Sunday, June 5, 2016 - 10:11:08 AM

File

JALEXIS_ID14698.pdf
Files produced by the author(s)

Identifiers

Citation

Mathilde Guérin, Joël Alexis, Eric Andrieu, Lydia Laffont-Dantras, Williams Lefebvre, et al.. Identification of the metallurgical parameters explaining the corrosion susceptibility in a 2050 aluminium alloy. Corrosion Science, Elsevier, 2016, 102, pp.291-300. ⟨10.1016/j.corsci.2015.10.020⟩. ⟨hal-01264384⟩

Share

Metrics

Record views

189

Files downloads

609