Mécanismes d'usure des outils coupants en usinage à sec de l'alliage de titane aéronautique Ti-6Al-4V

Mohammed Nouari (1) , Madalina Calamaz (2) , Franck Girot (2)

1 LEMTA - Laboratoire d'Energétique et Mécanique Théorique et Appliquée
2 I2M - Institut de Mécanique et d'Ingénierie de Bordeaux

In the present study, the titanium alloy 'Ti-6Al-4V' is orthogonally machined without cutting fluid. During experiments, the cemented carbide tools were rigidly mounted on the tool holder with rake angles of 0°, 15° and 30°. Three cutting speeds of 15, 30 and 60 m/min and three feeds of 0.1, 0.2, and 0.3 mm were selected. The experimental results show that the tool catastrophic failure occurs just after the first pass of cutting for all cutting parameters when using the tool with a rake angle of 30°. The analysis of the tribological parameters (friction, temperature, contact pressure) shows the effect of the machining parameters and the tool geometry on the damage modes during dry machining. To cite this article: M. Nouari et al., C. R. Mecanique 336 (2008).

Mots clés: Analyse par éléments finis; Damage; Degradation modes; Dry machiningTi-6Al-4V; Endommagement; Finite Element Analysis; Modes d'endommagement; Paramètres tribologiques; Tribological parameters; Usinage à sec du Ti-6Al-4V

Domaines: Matériaux; Mécanique [physics.med-ph]; Génie mécanique [physics.class-ph]; Génie mécanique [physics.class-ph]; Matériaux et structures en mécanique [physics.class-ph]; Matériaux et structures en mécanique [physics.class-ph]; Mécanique des matériaux [physics.class-ph]; Mécanique des matériaux [physics.class-ph]

Mohammed Nouari, Madalina Calamaz, Franck Girot. Mécanismes d'usure des outils coupants en usinage à sec de l'alliage de titane aéronautique Ti-6Al-4V. Comptes Rendus Mécanique, 2008, 336 (10), pp.772-781. ⟨10.1016/j.crme.2008.07.007⟩. ⟨hal-01018077⟩