Autogenous deformations of cement pastes

Pierre Mounanga (1) , Véronique Baroghel-Bouny (2) , Ahmed Loukili (1) , Abdelhafid Khelidj (1)

1 GeM - Institut de Recherche en Génie Civil et Mécanique
2 IFSTTAR - Institut Français des Sciences et Technologies des Transports, de l'Aménagement et des Réseaux

A micro-macro experimental study has been performed, from the end of mixing up to 2 years, on a set of plain cement pastes prepared with the same type I ordinary Portland cement (OPC) and various water-to-cement ratios (W/C), and cured at various constant temperatures. In this part I of the paper, volumetric autogenous shrinkage has been analysed in relation to various parameters characterizing the hydration process: chemical shrinkage, degree of hydration of the cement, Ca(OH)(2) content and Vicat setting times, within the early-age period (<= 24 h). The effects of the curing temperature (ranging from 10 up to 50 degrees C) have in particular been investigated. Its effects recorded on both the rate and the magnitude of volumetric autogenous shrinkage vs. time have pointed out the irrelevance of the usual maturity concept to describe such phenomenon within the whole early-age period. An improved maturity concept has hence been proposed. It is based on separating the early-age period in different phases and on using chemical shrinkage data for the calculation of the apparent activation energy applied to the prediction of autogenous deformations occurring after the setting period. Furthermore, micro-macro relationships have been pointed out, illustrating in particular the determining role of Ca(OH)(2).

Mots clés: Early age; Cement paste; Hydration; Maturity concept; Shrinkage

Domaines: Mécanique [physics.med-ph]; Matériaux

Pierre Mounanga, Véronique Baroghel-Bouny, Ahmed Loukili, Abdelhafid Khelidj. Autogenous deformations of cement pastes: Part I. temperature effects at early age and micro-macro correlations. Cement and Concrete Research, 2006, 36 (1), pp.110-122. ⟨10.1016/j.cemconres.2004.10.019⟩. ⟨hal-01005281⟩