Magnetic structure of the Mn5Si3-type Er5Si3 compound - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Intermetallics Année : 2011

Magnetic structure of the Mn5Si3-type Er5Si3 compound

Résumé

Neutron diffraction study has been performed on the Er5Si3 compound (hexagonal Mn5Si3-type, hP16, P6(3)/mcm) to understand its magnetic structure. The temperature dependent neutron diffraction results prove that this compound shows a complex antiferromagnetic ordering with sine modulated magnetic moments collinear to the c axis, presenting three subsequent changes in magnetization at similar to 29 K, 13 K and 10 K on cooling. The high-temperature magnetic component of Er5Si3 (C-3v, magnetic point group, P31m magnetic space group, K-1 = [0, 0, +/- 0.277(2)]) exists from 29 K to 10 K, whereas low-temperature magnetic component (symmetry C-1v, magnetic point group, Pm magnetic space group, K-2 = [0, +/- 1/4, 0]) exists from 13 K down to 1.5 K. The low-temperature and high-temperature magnetic components coexist between 13 K and 10 K.

Dates et versions

hal-00989241 , version 1 (09-05-2014)

Identifiants

Citer

A. V. Morozkin, Olivier Isnard, S.A. Granovsky. Magnetic structure of the Mn5Si3-type Er5Si3 compound. Intermetallics, 2011, 19, pp.871-875. ⟨10.1016/j.intermet.2011.02.004⟩. ⟨hal-00989241⟩

Collections

UGA CNRS NEEL
63 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More