On the Liquid/Solid Phase Equilibria in the Al-Rich Corner of the Al-Si-Ti Ternary System

Abstract : The nature of liquid-solid phase equilibria in the Al-rich corner of the Al-Si-Ti system are determined by drawing three isothermal sections at 620, 680 and 727 C. The solubility of Ti in Al-Si liquids is determined for four different compositions (0, 9, 13 and 18 at.%Si) at temperature below 800 C. Combination of the two sets of experimental results leads to an attempt of liquidus projection. The primary crystallization surface of Al3Ti is found to extend up to 9.5 at.%Si in the liquid phase at 620 C and 11 at.%Si at 727 C. The solubility of Ti is found to be not significantly dependent on the Si content of the liquid. From DSC measurements and deduction on microstructure, the last invariant reaction of the solidification path is found to be quasi-peritectic: L + Tau1-Ti7Al5Si12 -> Al + Si.
Type de document :
Article dans une revue
Journal of Phase Equilibria and Diffusion, Springer Verlag, 2014, 35 (2), pp.137. 〈10.1007/s11669-014-0282-1〉
Domaine :
Liste complète des métadonnées

Littérature citée [27 références]  Voir  Masquer  Télécharger

https://hal.archives-ouvertes.fr/hal-00960314
Contributeur : Olivier Dezellus <>
Soumis le : lundi 17 mars 2014 - 23:50:09
Dernière modification le : mercredi 2 mai 2018 - 10:21:56
Document(s) archivé(s) le : mardi 17 juin 2014 - 14:24:17

Fichier

Dezellus_AlSiTi_JPED_2014_HAL....
Fichiers éditeurs autorisés sur une archive ouverte

Identifiants

Citation

Olivier Dezellus, B. Gardiola, J. Andrieux, Marc Lomello-Tafin, J.-C. Viala. On the Liquid/Solid Phase Equilibria in the Al-Rich Corner of the Al-Si-Ti Ternary System. Journal of Phase Equilibria and Diffusion, Springer Verlag, 2014, 35 (2), pp.137. 〈10.1007/s11669-014-0282-1〉. 〈hal-00960314〉

Partager

Métriques

Consultations de la notice

323

Téléchargements de fichiers

419