Rheological Behavior of Pure Binary Ni-Nb Model Alloys - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Science Forum Année : 2010

Rheological Behavior of Pure Binary Ni-Nb Model Alloys

Résumé

This experimental work deals with the influence of niobium additions to high purity nickel on dynamic recrystallization behavior during hot working. Various high-purity alloys were prepared (unalloyed Ni and Ni-0.01, 0.1, 1 and 10 wt % Nb) and deformed to high strains by hot torsion tests to characterize the theological behavior within the range 800 1000 degrees C at strain rates of 0.03, 0.1 and 0.3 s(-1). Niobium additions strongly increased the flow stress. To quantify such behavior, the strain-hardening parameter h and dynamic-recovery parameter r in the Yoshie-Laasraoui-Jonas constitutive equation were determined from the initial part of the experimental stress-strain curves (i e., at strains before the stress peak) in which dynamic recrystallization does not alter the mechanical behavior. A table showing the variation of h and r as a function of strain rate, temperature, and niobium content was compiled and used to fit a simple empirical model for predicting h and r from the deformation conditions and alloy composition. In addition, microstructures were determined by optical metallography and SEM/EBSD. Based on this work, it appears that niobium additions noticeably refine the steady-state grain size by considerably decreasing the kinetics of dynamic recrystallization in nickel.
Fichier principal
Vignette du fichier
piot2010.pdf (262.94 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-00854887 , version 1 (23-06-2022)

Licence

Paternité - Pas d'utilisation commerciale

Identifiants

Citer

David Piot, Frank Montheillet, S.L Semiatin. Rheological Behavior of Pure Binary Ni-Nb Model Alloys. Materials Science Forum, 2010, 638-642, pp.2700-2705. ⟨10.4028/www.scientific.net/MSF.638-642.2700⟩. ⟨hal-00854887⟩

Collections

INSTITUT-TELECOM
21 Consultations
10 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More