Critical Temperature Range in Standard and Ni-bearing Spheroidal Graphite Cast Irons

Abstract : Describing the conditions for reaustenitization of spheroidal graphite cast irons is of interest for their heat-treatment after casting, e.g. for manufacturing austempered ductile irons. Differential thermal analysis has been used to characterize the direct eutectoid transformation and the reverse transformation, i.e. the reaustenitization. This has been applied to a standard and a Ni-bearing alloy, with a ferritic matrix for the former, both a ferritic and a pearlitic matrix for the latter. The results are discussed in relation with the stable and metastable three phase fields. While earlier description of the direct eutectoid transformation is confirmed, the one for reverse eutectoid has been found more complex and is amended.
Document type :
Journal articles
Complete list of metadatas

Cited literature [10 references]  Display  Hide  Download

https://hal.archives-ouvertes.fr/hal-00853822
Contributor : Open Archive Toulouse Archive Ouverte (oatao) <>
Submitted on : Friday, August 23, 2013 - 4:38:22 PM
Last modification on : Friday, January 10, 2020 - 9:08:21 PM
Long-term archiving on: : Sunday, November 24, 2013 - 4:16:13 AM

File

Ghergu_9057.pdf
Files produced by the author(s)

Identifiers

Collections

Citation

Roxana Maria Ghergu, Jon Sertucha, Yannick Thebault, Jacques Lacaze. Critical Temperature Range in Standard and Ni-bearing Spheroidal Graphite Cast Irons. ISIJ international, Iron & Steel Institute of Japan, 2012, vol. 52, pp. 2036-2041. ⟨10.2355/isijinternational.52.2036⟩. ⟨hal-00853822⟩

Share

Metrics

Record views

287

Files downloads

188