Boson peak of alkali and alkaline earth silicate glasses: Influence of the nature and size of the network-modifying cation
Résumé
The influence of the size of the alkaline earth cation on the boson peak of binary metasilicate glasses, MSiO3 (M = Mg, Ca, Sr, Ba), has been investigated from vibrational densities of states determined by inversion of low-temperature heat capacities. As given both by C-p/T-3 and g(omega)/omega(2), the intensity of the boson peak undergoes a 7-fold increase from Mg to Ba, whereas its temperature and frequency correlatively decrease from 18 to 10 K and from 100 to 20 cm(-1), respectively. The boson peak results from a combination of librations of SiO4 tetrahedra and localized vibrations of network-modifying cations with non-bridging oxygens whose contribution increases markedly with the ionic radius of the alkaline earth. As a function of ionic radii, the intensity for Sr and Ba varies in the same way as previously found for alkali metasilicate glasses. The localized vibrations involving alkali and heavy alkaline earth cations appear to be insensitive to the overall glass structure. Although the new data are coherent with an almost linear relationship between the temperature of the boson peak and transverse sound velocity, pure SiO2 and SiO2-rich glasses make marked exceptions to this trend because of the weak transverse character of SiO4 librations. Finally, the universality of the calorimetric boson peak is again borne out because all data for silicate glasses collapse on the same master curve when plotted in a reduced form (C-P/T-3)/(CP/T-3)(b) vs. T/T-b. (C) 2012 American Institute of Physics. [doi: 10.1063/1.3677194]