Development of nickel phosphorus coatings containing micro particles of talc phyllosilicates - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Chemistry and Physics Année : 2013

Development of nickel phosphorus coatings containing micro particles of talc phyllosilicates

Résumé

The present work aims to characterized nickel phosphorus coatings co-deposited with talc particles on steel. The NiP-talc composite deposits were developed to serve as hard coatings with a lubricating effect at 600 C. This process, which is free of hexavalent chromium, could provide a reliable substitute for the electrodeposition of hard chromium coating used in industrial applications. Local responses to static and dynamic mechanical loading have been obtained by nano- and microhardness, microtensile and nanoscratch testing. The hardness and stiffness values slightly decrease when the amount of talc increases for untreated coatings. In contrast, a 420 C heat treatment leads to high hardness and Young's modulus values due to crystallization. Moreover, a 600 C heat treatment lowers these values through overageing. A 420 C heat treatment greatly improves the adherence and the cohesion of the coatings containing talc.
Fichier principal
Vignette du fichier
Alexis_8491.pdf (1.72 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00828234 , version 1 (30-05-2013)

Identifiants

Citer

Joël Alexis, Clélia Gaussens, Bernard Etcheverry, Jean-Pierre Bonino. Development of nickel phosphorus coatings containing micro particles of talc phyllosilicates. Materials Chemistry and Physics, 2013, pp. 723-733. ⟨10.1016/j.matchemphys.2012.09.049⟩. ⟨hal-00828234⟩
135 Consultations
539 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More