Effect of iron phase on the strengthening of lateritic-based "geomimetic" materials

Résumé

The present work aims to investigate the action of associated iron species contained in lateritic clays in the strengthening process of "geomimetic" materials (compressive strength of 12 MPa). The starting products are a lateritic clay from Cameroon, fulvic acid and lime. The synthesis involves acidic and alkaline reactions followed by a curing period of 18 days at 60 °C under water-saturated atmosphere. Since goethite (α-FeOOH), hematite (α-Fe2O3) and ferrihydrite (5Fe2O3*9H2O) are the main iron compounds in the raw clay, investigations have been carried out to identify to which extend each of these phases participates in the consolidation process. It appears that hematite and ferrihydrite may contribute to the consolidating mechanism since the as obtained "geomimetic" products exhibit characteristic compressive strength of 8.3 and 4.5 MPa respectively. Besides, the use of goethite leads to consolidated products with characteristic compressive strength of 6.5 MPa. The strengthening is effective when the synthesis of iron species is performed separately (no direct precipitation onto kaolin particles). Moreover, among the various model samples tested, only those elaborated with goethite were resistant towards water seeping and wearing. Hence, goethite is considered as the major active phase in the dissolution precipitation reaction which leads to bridging ferric gels.

Dates et versions

hal-00745732 , version 1 (26-10-2012)

Identifiants

Citer

Gisèle Laure Lecomte-Nana, Hervé Goure-Doubi, Agnès Smith, Alain Wattiaux, Gilles Lecomte. Effect of iron phase on the strengthening of lateritic-based "geomimetic" materials. Applied Clay Science, 2012, 70, pp.14-21. ⟨10.1016/j.clay.2012.09.014⟩. ⟨hal-00745732⟩
66 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More