Y. Yokoyama (1) , K. Fujita (2) , A.R. Yavari (3) , A. Inoue (1)

1 WPI-AIMR - WPI Advanced Institute for Materials Research
2 Dept Mech. Engn. Ube Natl Coll. Technol. Yamaguchi
3 SIMaP - Science et Ingénierie des Matériaux et Procédés

A new bulk glassy alloy (BGA) showing macroscopic tensile plastic elongation at room temperature has been developed in the hypoeutectic Zr-Ni-Cu-Al alloy system. The hypoeutectic Zr-Ni-Cu-Al BGA shows a high Poisson's ratio, a low Young's modulus, and is highly malleable in compression. It exhibits a Poisson's ratio of 0.39, a Young's modulus of 73 GPa, and a distinct tensile plastic elongation of about 1.7% at room temperature with necking due to the operation of many shear bands. The tensile plastic deformability seems to originate from modifications of the glass structure with increasing the number of Zr-Zr atomic pairs in the hypoeutectic composition

Mots clés: tensile testing; metallic glasses; mechanical-properties; amorphous-alloys; structural; relaxation; supercooled liquids; deformation; ductility; behavior; order; microstructure

Domaines: Matériaux; Matériaux

Y. Yokoyama, K. Fujita, A.R. Yavari, A. Inoue. Malleable hypoeutectic Zr-Ni-Cu-Al bulk glassy alloys with tensile plastic elongation at room temperature. Philosophical Magazine Letters, 2009, 89 (5), pp.322-324. ⟨10.1080/09500830902873575⟩. ⟨hal-00446978⟩