Viscoelastic properties of wood across the grain measured under water-saturated conditions up to 135°C: evidence of thermal degradation
Résumé
In this paper, the viscoelastic properties of wood under water-saturated conditions are investigated from 10°C to 135°C using the WAVET* apparatus. Experiments were performed via harmonic tests at two frequencies (0.1 Hz and 1 Hz) for several hours. Four species of wood were tested in the radial and tangential material directions: oak (Quercus sessiliflora), beech (Fagus sylvatica), spruce (Picea abies) and fir (Abies pectinata). When the treatment is applied for several hours, a reduction of the wood rigidity is significant from temperature values as low as 80-90°C, and increases rapidly with the temperature level. The storage modulus of oak wood is divided by a factor two after three hours of exposure at 135°C. This marked reduction in rigidity is attributed to the hydrolysis of hemicelluloses. The softening temperature of wood is also noticeably affected by hygrothermal treatment. After three short successive treatments up to 135°C, the softening temperature of oak shifted from 79°C to 103°C, at a frequency of 1 Hz. This reduction in mobility of wood polymers is consistent with the condensation of lignins observed by many authors at this temperature level. In the same conditions, fir exhibited a softening temperature decreasing of about 4°C. In any case, the internal friction clearly raises.
Origine : Fichiers produits par l'(les) auteur(s)
Loading...