Effect of hydrostatic pressure on elastic properties of ZDTP tribofilms

Karim Demmou (1) , Sandrine Bec (1) , Jean-Luc Loubet (1)

1 LTDS - Laboratoire de Tribologie et Dynamique des Systèmes

Previous studies have shown that the elastic properties of Zinc Dialkyl-dithiophosphate (ZDTP) tribofilms measured by nanoindentation increase versus applied pressure (Anvil effect) [1, 2]. The aim of this paper is to demonstrate that, up to 8 GPa, this increase is a reversible phenomenon. A ZDTP tribofilm has been produced on "AISI 52100" steel substrate using a Cameron-Plint tribometer. After its formation, a hydrostatic pressure of about 8 GPa was applied during one minute on the tribofilm using a large radius steel ball ("Brinell-like" test). Nanoindentation tests were performed with a Berkovich tip on pads in order to measure and compare the mechanical properties of the tribofilm inside and outside the macroscopic plastically deformed area. Careful AFM observations have been carried out on each indent in order to take into account actual contact area. No difference in elastic properties was observed between the two areas: tribofilm modulus and pressure sensitivity are the same inside and outside the residual hemispherical print. This demonstrates that Anvil effect is a reversible phenomenon in the studied pressure range.

Mots clés: Nanoindentation; Hardness; Young's Modulus; Zinc dialkyl-dithiophosphate; ZDTP; tribofilm; Hydrostatic pressure

Domaines: Mécanique [physics.med-ph]; Matériaux; Mécanique des matériaux [physics.class-ph]; Mécanique des matériaux [physics.class-ph]

Karim Demmou, Sandrine Bec, Jean-Luc Loubet. Effect of hydrostatic pressure on elastic properties of ZDTP tribofilms. 2007. ⟨hal-00158279⟩