Adhesion forces due to nano-triboelectrification between similar materials
Résumé
Contact electrification and triboelectrification are well-known in the case of dissimilar materials, however the case of charge exchange during friction between nominally identical insulating materials is less documented. We experimentally investigated the triboelectrification between two smooth monocrystalline α-Al 2O 3 (sapphire) antagonists by surface force measurements with a Surface Force Apparatus (SFA). The force between a sphere and a plane, both in sapphire, was measured as a function of the sphere-plane distance D, before and after nano-friction tests, under dry argon atmosphere. Respective contributions of van der Waals, water meniscus and electrostatic forces were determined. The estimated Hamaker constant was in good agreement with the Lifshitz theory, and the dominant meniscus attraction at low separation could be overcome with small radius sphere. We demonstrated that electrostatic forces were generated by the nano-friction test and we quantified the adhesion that results from this contact-electrification. In the first stage of the unloading process, the short range electrostatic force was found to vary both with time and distance D. Experimental results were correlated with surface densities of mobile charges on the two surfaces, and the time-dependence was related to classical surface transport phenomena on alumina surfaces.
Fichier principal
2004Guerret-Piecourt_et_al_Adhesion_forces_due_to_nano-triboelectrification.pdf (960.86 Ko)
Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)