The Characterization of the oxide films formed at the surface of Ni-base alloys in pressurized water reactors primary coolant by transmission electron microscopy

Abstract : The oxide film formed on nickel-based alloys in Pressurized Water Reactors (PWR) primary coolant conditions (325°C, aqueous media) has been investigated by Transmission Electron Microscopy (TEM). TEM observations revealed an oxide layer divided in two parts. The internal layer was mainly composed of a continuous spinel layer, identified as a mixed iron and nickel chromite (Ni(1-x)FexCr2O4). Moreover, nodules of Cr2O3 were present at the interface between this spinel and the alloy. The external layer is composed of large crystallites corresponding to a spinel structure rich in iron (Ni(1-z)Fe(2+z)O4) resulting from precipitation phenomena. The influence of alloy surface defects was also studied underlining two main consequences on the formation of the passive film e.g. the internal layer. On one hand, the growth kinetics of the internal spinel rich in chromium increased with the surface defect density. Besides that, when the defect density increased, the oxide scale became more finely crystallized. This result agrees with a growth mechanism due to a rate limiting process of diffusion through the grain boundaries of the oxide. On the other hand, the quantity of Cr2O3 nodules increased with the number of surface defects, revealing that the nodules nucleated preferentially at defect location.
Complete list of metadatas

Cited literature [4 references]  Display  Hide  Download

https://hal-emse.ccsd.cnrs.fr/emse-00590705
Contributor : Andrée-Aimée Toucas <>
Submitted on : Thursday, May 5, 2011 - 10:24:30 AM
Last modification on : Thursday, February 7, 2019 - 2:49:21 PM
Long-term archiving on : Saturday, August 6, 2011 - 2:36:36 AM

File

MP-MSF-595-598-539-orig.pdf
Files produced by the author(s)

Identifiers

Citation

Mohamed Sennour, Loïc Marchetti, Stéphane Perrin, Régine Molins, Michèle Pijolat, et al.. The Characterization of the oxide films formed at the surface of Ni-base alloys in pressurized water reactors primary coolant by transmission electron microscopy. 7th International Symposium on High Temperature Corrosion and Protection of Materials, May 2008, Les Embiez, France. pp.539-547, ⟨10.4028/www.scientific.net/MSF.595-598.539⟩. ⟨emse-00590705⟩

Share

Metrics

Record views

418

Files downloads

460