Cavity growth and rupture of β-treated zirconium: A crystallographic model
Résumé
This study aims to understand the damage mechanisms observed in β-treated zirconium. Damage voids are characterized by a tubular morphology with hexagonal cross-section; their growth kinetics is determined experimentally. From these observations, a model based on the principle of creation of free surface by crystallographic slip permits one to explain the stability of the hexagonal shape and to predict a growth rate closer to the experimental value than traditional models. This improvement is due to the sensitivity of the free surface creation mechanism to the stress concentration factor k, which can not be accounted for in models based on continuum mechanics.
Cette étude a pour but de comprendre les mécanismes d'endommagement observés dans le zirconium traité β. L'endommagement est caractérisé par des cavités de forme tubulaire à section hexagonale; leur cinétique de croissance est déterminée expérimentalement. A partir de ces observations, un modèle basé sur le principe de création de surface libre par glissement cristallographique permet d'expliquer la stabilité de la forme hexagonale et de prévoir une vitesse de croissance plus proche de la valeur expérimentale que celles prévues par les modèles traditionnels. L'amélioration de la prédiction est due à la sensibilité des mécanismes de création de surface libre vis à vis du facteur de concentration de contrainte k, ce qui ne peut être pris en compte dans un modèle basé sur la mécanique des milieux continus.
Origine : Fichiers produits par l'(les) auteur(s)