Influence of alloying on the tensile strength and electrical resistivity of silver nanowire: copper composites macroscopic wires - Fédération de recherche « Matière et interactions » Accéder directement au contenu
Article Dans Une Revue Journal of Materials Science Année : 2021

Influence of alloying on the tensile strength and electrical resistivity of silver nanowire: copper composites macroscopic wires

Résumé

Composite powders made up of 1 vol. %Ag nanowires (NW) dispersed in Cu were prepared and consolidated into cylinders by spark plasma sintering. One cylinder was sintered at only 400 °C resulting in a nanocomposite sample with no dissolution of the Ag NW into the Cu matrix. The second cylinder was sintered at 600 °C and the Ag NW are dissolved forming Ag/Cu alloy NW. The cylinders served as starting materials for room temperature wire-drawing, enabling the preparation of wires of decreasing diameters. The microstructure of the cylinders and the wires was investigated by electron microscopy and associated techniques. The tensile strength and electrical resistivity were measured at 293 K and 77 K. The nanocomposite and alloy wires show similar UTS values (1100 MPa at 77 K), but alloying, although spatially limited, provoked a significant increase in electrical resistivity (0.56 µΩ cm at 77 K) compared to the nanocomposite wires (0.49 µΩ cm at 77 K).

Domaines

Matériaux
Fichier principal
Vignette du fichier
Tardieu_27124.pdf (2.77 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03108715 , version 1 (13-01-2021)

Identifiants

Citer

Simon Tardieu, David Mesguich, Antoine Lonjon, Florence Lecouturier-Dupouy, Nelson Ferreira, et al.. Influence of alloying on the tensile strength and electrical resistivity of silver nanowire: copper composites macroscopic wires. Journal of Materials Science, 2021, 56 (7), pp.4884-4895. ⟨10.1007/s10853-020-05556-9⟩. ⟨hal-03108715⟩
299 Consultations
30 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More