Thermomagnetically patterned micromagnets
Dumas-Bouchiat F., Zanini L.-F., Kustov S., Dempsey N., Grechishkin R., Hasselbach K., Orlianges J.-C., Champeaux C., Catherinot A., Givord D.
Applied Physics Letters 96 (2010) 102511-1-102511-3 - http://hal.archives-ouvertes.fr/hal-00569295
Type de publication : Articles dans des revues avec comité de lecture
Titre : Thermomagnetically patterned micromagnets
Auteur(s) : Frédéric Dumas-Bouchiat 1, Luiz-Fernando Zanini 1, S. Kustov 2, Nora Dempsey 1, R. Grechishkin 3, Klaus Hasselbach () 1, Jean-Christophe Orlianges 4, Corinne Champeaux () 4, Alain Catherinot () 4, Dominique Givord 1
Laboratoire :
1 :  Institut Néel (NEEL)
http://www.neel.cnrs.fr/
CNRS : UPR2940 – Université Joseph Fourier - Grenoble I – Institut National Polytechnique de Grenoble (INPG)
25 avenue des Martyrs - BP 166 38042 GRENOBLE CEDEX 9
France
2 :  Laboratoire de Génie Electrique de Grenoble (G2ELab)
http://www.G2Elab.grenoble-inp.fr
CNRS : UMR5269 – Université Joseph Fourier - Grenoble I – Institut Polytechnique de Grenoble - Grenoble Institute of Technology
Domaine universitaire 961. rue de la Houille Blanche BP 46 38402 ST MARTIN D HERES CEDEX
France
3 :  Laboratory of Magnetoelectronics
Tver State University
170000 Tver
Russie, Fédération De
4 :  Science des Procédés Céramiques et de Traitements de Surface (SPCTS)
http://www.unilim.fr/spcts/
CNRS : UMR6638 – Université de Limoges – Ecole Nationale Supérieure de Céramique Industrielle – Institut des Procédés Appliqués aux Matériaux
SPCTS, Centre Européen de la Céramique, 12 Rue Atlantis, 87068 LIMOGES CEDEX
France
Équipe de recherche : Axe 2 : procédés de traitements de surface
Résumé : Thermomagnetic patterning TMP of 4 m thick high performance NdFeB hard magnetic films deposited on Si substrates has been achieved using single pulsed laser irradiation. Uniaxially magnetised chessboard and stripe patterns with lateral feature sizes in the range 50–100 m were produced. The depth of reversal was estimated, using both global vibrating sample magnetometry and localized scanning Hall probe measurements, to be in the range of 1.1–1.2 m. A simple model provides semiquantitative agreement with the experimental results. A linear Halbach array was fabricated to demonstrate the potential of TMP for the realization of complex multidirectional microflux sources.
Langue du texte
intégral :		 Anglais
Journal :
Applied Physics Letters (Appl. Phys. Lett.)
Publisher American Institute of Physics (AIP)
ISSN 0003-6951 (eISSN : 0003-6951)
Audience : internationale
Date de publication : 2010
Volume : 96
Page, identifiant, ... : 102511-1-102511-3
hal-00569295, version 1
http://hal.archives-ouvertes.fr/hal-00569295
oai:hal.archives-ouvertes.fr:hal-00569295
Contributeur : Martine Segear <>
Soumis le : Jeudi 24 Février 2011, 16:25:19
Dernière modification le : Vendredi 11 Mars 2011, 09:16:54