%0 Journal Article
%T Impact of PP Impurities on ABS Tensile Properties: Computational Mechanical Modelling Aspects
%+ Polymères Composites et Hybrides (PCH - IMT Mines Alès)
%+ Durabilité des éco-Matériaux et Structures (DMS)
%A Signoret, Charles
%A Caro-Bretelle, A. S.
%A Lopez-Cuesta, José-Marie
%A Ienny, Patrick
%A Perrin, Didier
%< avec comité de lecture
%@ 2073-4360
%J Polymers
%I MDPI
%V 13
%N 10
%P 1647
%8 2021
%D 2021
%R 10.3390/polym13101647
%K polymer recycling
%K WEEE
%K predictive modeling
%K volume change
%Z Engineering Sciences [physics]/Mechanics [physics.med-ph]/Mechanics of materials [physics.class-ph]
%Z Chemical Sciences/PolymersJournal articles
%X Recycling of plastics is hindered by their important variety and strong incompatibility. However, sorting technologies bear costs and meet limits. Very high purities (<2 wt%) are difficult to reach. Yet, such rates may be detrimental to functional properties. In this work, an ABS matrix (major plastic in Waste of Electrical and Electronic Equipments) was filled with 4 wt% of PP to mimic impurities in ABS after recycling. PP-g-MA was introduced in the blend to improve the compatibility. A finite element model was developed from the mechanical behavior of each component. ABS and PP were individually characterized from tensile tests instrumented with photomechanics and their behaviors were modelled through a set of numerical parameters (elasto-visco-plasticity with a Gurson’s criterion behavior). Comparison between the determinist model results and the experimental data (strength, volumetric variation) shows that this type of modelling could be a predictive tool in order to anticipate composite mechanical properties and to understand micromechanisms of deformation (damage, cavitation). The main result is that PP introduced at 4 wt% into ABS does not alter the static mechanical properties despite polymers incompatibility. The addition of PP-g-MA modifies the local properties and possibly conduct to a premature breakage of the polymer blend.
%G English
%2 https://imt-mines-ales.hal.science/hal-03235511/document
%2 https://imt-mines-ales.hal.science/hal-03235511/file/polymers-13-01647.pdf
%L hal-03235511
%U https://imt-mines-ales.hal.science/hal-03235511
%~ INSTITUT-TELECOM
%~ CNRS
%~ EM-ALES
%~ LMGC
%~ MIPS
%~ UNIV-MONTPELLIER
%~ INSTITUTS-TELECOM
%~ UM-2015-2021