Effect of interlamellar spacing on the elastoplastic behavior of C70 pearlitic steel: Experimental results and self-consistent modeling

Résumé

The effect of pearlite microstructure characteristics on strength and deformation of C70 pearlitic steel was investigated. Tensile tests under X-ray diffraction coupled with self-consistent model have been used to identify the role of interlamellar spacing on the ferrite plasticity parameters and residual stress induced by plasticity. Tests have been carried out on two pearlitic microstructures with interlamellar spacing Sp = 170 and 230 nm respectively. Ferrite critical shear stresses ðs0c ðaÞÞ are equal to 75-86 MPa for interlamellar spacing Sp = 230 nm and 105-120 MPa for interlamellar spacing Sp = 170 nm. Moreover, the compressive residual stress measured in ferrite phase is higher in elasto-plastically deformed sample (total strain of E11 = 1.2%) having larger interlamellar spacing (rR Fea ¼ 161 MPa for Sp = 230 nm and rR Fea ¼ 77 MPa for Sp = 170 nm).
Fichier principal
Vignette du fichier
PIMM_-_MD-YAHYAOUI-2014.pdf (1.18 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00980349 , version 1 (04-07-2014)

Identifiants

Citer

Houda Yahyaoui, H Sidhom, Chedly Braham, A. Baczmanski. Effect of interlamellar spacing on the elastoplastic behavior of C70 pearlitic steel: Experimental results and self-consistent modeling. Materials & Design, 2014, 55, pp.888-897. ⟨10.1016/j.matdes.2013.10.062⟩. ⟨hal-00980349⟩
106 Consultations
1045 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More