METALLURGY, HRTEM, MAGNETIC-PROPERTIES AND SPECIFIC-HEAT OF TL2BA2CU1O6+DELTA 90 K-SUPERCONDUCTORS OBTAINED BY A NEW PROCESS

Christine Opagiste (1) , M. Couach (1) , A.F. Khoder (1) , T. Graf (2) , A. Junod (2) , G. Triscone (2) , J. Muller (2) , T.K. Jondo (3) , J. -L. Jorda (3) , R. Abraham (3) , M. Th. Cohen-Adad (3) , L. A. Bursill (3) , O. Leckel (4) , M. G. Blanchin (4)

1 LCP - Laboratoire de Cryophysique
2 DPMC
3 Laboratoire de Physicochimie Minérale
4 LPM - Laboratoire de Physique des Matériaux

High-quality Tl2Ba2CuO6+delta (2201) compounds were synthesized using a high-pressure route. Starting from Tl2Ba2O5 and CuO, the reactions yielding either the orthorhombic or the tetragonal (superconducting) phases were carried out under 100 bar of oxygen or argon and helium, respectively. Preferential thallium losses are prevented and high sintering temperatures can be used to obtain pure samples with large 2201 grains. The experiments performed include metallographic examinations, X-ray diffraction, microprobe analysis, plasma emission spectroscopy, HRTEM, AC susceptibility, Meissner field cooling, hysteresis loops, normal-state susceptibility and specific heat measurements.

Mots clés: Superconductivity; Thallium compound; cuprates; high pressure synthesis; HRTEM; AC susceptibility; Specific heat

Domaines: Supraconductivité [cond-mat.supr-con]

Christine Opagiste, M. Couach, A.F. Khoder, T. Graf, A. Junod, et al.. METALLURGY, HRTEM, MAGNETIC-PROPERTIES AND SPECIFIC-HEAT OF TL2BA2CU1O6+DELTA 90 K-SUPERCONDUCTORS OBTAINED BY A NEW PROCESS. Physica C: Superconductivity and its Applications, 1993, 205 (3-4), pp.247-258. ⟨10.1016/0921-4534(93)90389-8⟩. ⟨hal-00569528⟩