THE FRACTURE OF DIAMOND COATINGS BY HIGH VELOCITY SAND EROSION

Robert Jk Wood (1) , David Wheeler (2)

1 School of Engineering Sciences
2 School of Engineering Sciences

This paper describes a study of the behaviour of diamond coatings when subjected to solid particle erosion from sand particles. The coatings were deposited by chemical vapour deposition (CVD) onto tungsten substrates and tested using a high velocity air-sand erosion test facility. The erosion tests were conducted using particle impact velocities of between 33 and 268 m s-1. Examination of the eroded test specimens showed that the principal damage features observed were circumferential cracks and pin-holes. Comparison with Hertz impact theory revealed that the measured circumferential crack diameters were more than double the predicted Hertzian contact diameter. Moreover, a trend of increasing circumferential crack diameter with coating thickness, which is not predicted by Hertz, was found. Instead, the crack diameters showed good agreement with those predicted by the theory of stress wave reinforcement, which is more commonly associated with liquid impact damage of brittle materials. During impact, the bulk compression and shear waves are reflected at the rear surface of debonded regions of the coating to return to the front surface and reinforce the Rayleigh surface wave, which generates a tensile stress. Where this stress exceeds the local tensile strength of the coating, a ring of cracks surrounding the area of impact is created. This hypothesis was supported by images acquired using scanning acoustic microscopy, which showed that circumferential cracks and pin-holes were only found on areas of the coating that had become delaminated by multiple particle impacts during the erosion tests.

Mots clés: Physical Sciences

Robert Jk Wood, David Wheeler. THE FRACTURE OF DIAMOND COATINGS BY HIGH VELOCITY SAND EROSION. Philosophical Magazine, 2009, 89 (03), pp.285-310. ⟨10.1080/14786430802616557⟩. ⟨hal-00514004⟩