SANS response of VVER440-type weld material after neutron irradiation, post-irradiation annealing and reirradiation

Andreas Ulbricht (1) , Frank Bergner (2) , Juergen Boehmert (1) , Matti Valo (3) , Marie-Helene Mathon (4) , Andre Heinemann (5)

1 Institute of Safety Research
2 Institute of Safety Research
3 VTT Industrial Systems
4 LLB - UMR 12 - Laboratoire Léon Brillouin
5 BENSC

It is well accepted that the reirradiation behaviour of reactor pressure vessel (RPV) steel after annealing can be different from the original irradiation behaviour. We present the first small-angle neutron scattering (SANS) study of neutron irradiated, annealed and reirradiated VVER440-type RPV weld material. The SANS results are analysed both in terms of the size distribution of irradiation-induced defect/solute atom clusters and in terms of the ratio of total and nuclear scattering intensity in a saturation magnetic field (A-ratio). The measured A-ratio is compared with calculations performed on the basis of the cluster composition reported for a similar weld material investigated by means of three-dimensional atom probe field ion microscopy. The observed deviation between both estimates and possible reasons for the discrepancy are discussed. Special emphasis is placed on the differences between the materials response to the original irradiation and to reirradiation after annealing. The results indicate that reirradiation-induced clusters are slightly different in their average composition and their formation saturates at a lower volume fraction than in the case of the original irradiation.

Mots clés: Physical Sciences

Andreas Ulbricht, Frank Bergner, Juergen Boehmert, Matti Valo, Marie-Helene Mathon, et al.. SANS response of VVER440-type weld material after neutron irradiation, post-irradiation annealing and reirradiation. Philosophical Magazine, 2007, 87 (12), pp.1855-1870. ⟨10.1080/14786430601102999⟩. ⟨hal-00513810⟩