Homogeneous Cu-Fe super saturated solid solutions prepared by severe plastic deformation

Résumé

A Cu-Fe nanocomposite containing 50 nm thick iron filaments dispersed in a copper matrix was processed by torsion under high pressure at various strain rates and temperatures. The resulting nanostructures were characterized by transmission electron microscopy, atom probe tomography and Mössbauer spectrometry. It is shown that -Fe filaments are dissolved during severe plastic deformation leading to the formation of a homogeneous supersaturated solid solution of about 12 at.% Fe in fcc Cu. The dissolution rate is proportional to the total plastic strain but is not very sensitive to the strain rate. Similar results were found for samples processed at liquid nitrogen temperature. APT data revealed asymmetric composition gradients resulting from the deformation induced intermixing. On the basis of these experimental data, the formation of the supersaturated solid solutions is discussed
Fichier principal
Vignette du fichier
intermixing_FeCu-Philos_Mag_HAL_2010.pdf (1.04 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00581021 , version 2 (17-06-2010)
hal-00581021 , version 1 (30-03-2011)

Identifiants

Citer

Xavier Quelennec, Alain Menand, Jean Marie Le Breton, Reinhard Pippan, Xavier Sauvage. Homogeneous Cu-Fe super saturated solid solutions prepared by severe plastic deformation. Philosophical Magazine, 2010, 90 (9), pp.1179-1195. ⟨10.1080/14786430903313682⟩. ⟨hal-00581021v2⟩
161 Consultations
206 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More